Product synopsis:
XTT - 6 pulp is high-powered composite modified starch, cohesion, film, good flexibility, wearability is superior to other serosal denatured starch. Can be used alone or in combination with PVA, and compared with other modified starch with PVA can reduce the 40-60 percent, can satisfy the cotton, hemp, polyester fiber, etc, and ZhongMi warp sizing of the fabric such as required.
Specifications:
Appearance: white powder
PH: 6.5-750
Viscosity: 18-22mpa. S (6%), 95 degrees NDJ 1.5h),
Hot viscosity stability: the volatility < 15%
The effective ingredient: 87 percent
The main advantage
In fiber has a strong force induces
* cook-resistance with PVA, while cooking
* subserosal flexibility
Thermal viscosity stability is good.
* ratio to operate
Using methods
The amount required XTT - 6 into mixing of water, steam and high-speed mixing boiling for 30 minutes, a small steam, braised plasma deposition.
In high-pressure barrels into the amount required XTT - 6, according to a boil plasma (general process of 120 degrees Celsius temperature preservation 30 minutes),
packing
25kg net weight of each bag
Product Description:
XTT-6 slurry line of high-performance composite modified starch, adhesive power and good film-forming, serosal flexibility, wear resistance is superior to other modified starch. Can be used alone or used with PVA, and compared with other modified starch PVA used in about 40-60% can be reduced to meet the cotton, linen, polyester, viscose and other fibers and high density fabrics such as warp sizing requirements.
Product specifications:
Appearance: white powder
PH value :6.5-7.5
Viscosity :18-22mpa. S (NDJ.6%, 95 ℃, 1.5h)
Hot viscosity stability: fluctuations in the rate of |